Effect of an additional bonding resin on the 5-year performance of a universal adhesive: a randomized clinical trial

Abstract

Objectives To evaluate the effect of the application of an additional hydrophobic bonding resin on the clinical performance of a universal adhesive applied in etch-and-rinse (ER) or self-etch adhesive (SE) strategy in non-carious cervical lesions (NCCLs) after 5 years. Materials and methods Scotchbond Universal Adhesive (3M Oral Care) was applied in 134 NCCLs of 39 subjects using different adhesion approaches: 3-step ER (3-ER), 2-step ER (2-ER), 2-step SE (2-SE), and 1-step SE (1-SE). Enamel and dentin were acid etched prior to application of the universal adhesive for the 3-ER and 2-ER groups. An extra layer of a hydrophobic bonding resin was applied for groups 3-ER and 2-SE. All lesions were restored with Filtek Supreme XTE resin composite (3M Oral Care). Restorations were evaluated at baseline and at 5 years using the modified USPHS criteria. Mann-Whitney U and Wilcoxon tests were performed, and the survival rates (retention/fracture) were analyzed using Kaplan-Meier and log-rank tests (p < 0.05). Results The recall rate was 66.7% at 5 years. The cumulative survival rate was 96.9% for 3-ER, 96.8% for 2-ER, 71.4% for 2-SE, and 81.3% for 1-SE strategies. The log-rank test was statistically significant (p = 0.006). Retention rates were 100% for both ER groups, 75% for 2-SE and 81.3% for 1-SE. At 5 years, 2- and 1-SE approaches showed similar retention rates, but lower than those for 3- and 2-ER. A significant decrease in retention rate was detected for 2-SE (p = 0.007) and 1-SE (p = 0.014) groups between baseline and 5 years. All groups, except 2-ER, showed an increase in marginal discoloration. For this parameter, significant differences were detected between 2-ER and 1-SE (p = 0.004). Conclusions The addition of a hydrophobic bonding resin to the recommended application sequence of Scotchbond Universal Adhesive did not improve its clinical performance in NCCLs after 5 years. Higher retention rates were measured when this adhesive was applied in ER mode.