Examinando por Autor "Rieth, M."

Mostrando 1 - 2 de 2

Numerical and experimental development of cupronickel filler brazed joints for divertor and first wall components in DEMO fusion reactor
(Elsevier, 2023) Díaz-Mena, Víctor; de Prado, J.; Roldán, M.; Izaguirre, I.; Sánchez, M.; Rieth, M.; Ureña, A.
The brazeability of a cupronickel commercial alloy (Cu10Ni) was evaluated for its use as a filler alloy for high-temperature joining of tungsten to the reduced activation ferritic/martensitic steel EUROFER 97 (W-E) and between tungsten base materials (W-W) for its application at the first wall and divertor of future fusion reactors. In addition, given the importance of the residual stresses in these heterogenous joints, a study of the brazing conditions and the impact of the selected filler has been conducted using numerical software to understand its impact on the quality of the joint. Two thermal cycles were evaluated (1165 °C and 1190 °C) and selected based on the thermal characterization of the filler alloy. The microstructural examination revealed that, in W-E joints, nickel acts as an activator element, reacting and forming interfacial layers at the EUROFER 97 - Cu10Ni interface. In the case of the W-W joints, a lower level of diffusion phenomenon and metallurgical interaction between Cu10Ni and base materials were observed. The hardness profile indicated that the hardening process of EUROFER 97 was associated with the formation of untempered martensite. On the other hand, tungsten kept the received hardness. The mechanical characterization by shear test reported similar values between both types of joints carried out at 1190 °C but different when the temperature was increased (1165 °C), associated with the brittle character of tungsten and its lower metallurgical interaction. The numerical analysis of the brazing process carried out with ANSYS software shows that residual stresses are accumulated mainly at the interfaces. The information provided by the simulation shows, for a 50 µm filler thickness, the importance of mitigating the residual stress by selecting a filler with an intermediate Coefficient of Thermal Expansion (CTE) that alleviates mechanical stresses relative to the base materials.
W-EUROFER97 brazed joints using Ag, Au, and Cu-based fillers for energy applications: A microstructural and mechanical study
(Elsevier, 2024-12) Díaz-Mena, V.; Prado, J. de; Izaguirre, I.; Carreras, J.; Sánchez, M.; Rieth, M.; Ureña, A.
The brazeability of four different alloys (Au, Cu, and two Ag-based alloys) was evaluated for their use as filler materials in joints between EUROFER 97 and tungsten for its application in future fusion reactors. The study aims to analyze the operational brazeability in terms of deep microstructural analysis and mechanical behavior. In general, high metallic continuity was observed for all filler compositions. In the case of the joints brazed with the Au-based filler alloy, a homogeneous microstructure based on an Au-Pd-Fe-Ni solid solution is obtained. The use of Ag-based filler alloys produced a solid solution phase at the EUROFER97-braze interface, and a Ag-based phase in contact with the tungsten base material. Finally, with the cupronickel filler alloy, a braze constituted by two different Cu-Ni-Fe solid solution phases is obtained. Regarding the mechanical characterization, the Cu-based filler shows a lower hardness value, while the higher values were obtained with one of the Ag-based filler alloy. In the case of the shear tests, a maximum 304 ± 57 MPa strength is obtained for Au-based filler alloy brazed at 1171 ºC due to the combination of a homogeneous and toughness microstructure and the lack of intermetallic compounds in the braze