Influence of post cure time on the microhardness of self-adhesive resin cements inside the root canal

Abstract

Purpose: To compare the microhardness of several dual-cure, self-adhesive resin cements used to lute fiber posts at 24 hours and seven days after cementation.

Methods: Bovine incisors were selected to lute 15 fiber posts that were 12 mm long (FRC Postec Plus size 3, Ivoclar-Vivadent). Five resin cements were tested: Multilink Automix (Ivoclar-Vivadent), without light-curing, and the self-adhesive resin cements Maxcem Elite (Kerr), RelyX Unicem (3M ESPE), G-Cem (GC), and Smartcem 2 (Dentsply), which were light-cured for 40 seconds (LED Bluephase, Ivoclar-Vivadent). Each root was embedded in chemically cured acrylic resin and stored at 37°C for 24 hours. The roots were transversally sectioned into nine specimens that were each 1 mm thick, with three specimens corresponding to each root third. Indentations (100g, 30 seconds) were performed on each section in the resin cement, at 24 hours and seven days after cementation, using a Vickers digital microdurometer (Buehler). Data were analyzed by two-way analysis of variance, Student-Newman-Keuls test, and paired t-test (p<0.05).

Results: A significant influence was found (p<0.05) for the resin cement evaluated, the root third, and their interactions on microhardness values at 24 hours and seven days after post cementation. RelyX Unicem and G-Cem exhibited the highest microhardness values, whereas Multilink Automix presented the lowest. All resin cements suffered a decrease in microhardness according to root canal depth, with the exception of G-Cem and Multilink Automix at 24 hours and Smartcem 2 after seven days. After seven days, the evaluated resin cements showed a significant increase in microhardness values, with the exception of Maxcem Elite and Smartcem 2 at the coronal third.

Conclusions: Microhardness of the self-adhesive resin cements when used to lute fiber posts was material-dependent and higher values were obtained in the coronal third, revealing their sensitivity to light irradiation. More information regarding the polymerization reaction of these cements is warranted. According to the current results, microhardness values were significantly higher one week after post luting.