Effect of Heat Treatment on the Dry Sliding Wear Behavior of the Mg-3Zn-0.4Ca Alloy for Biodegradable Implants

Fecha

2023-01-10

Título de la revista

ISSN de la revista

Título del volumen

Editor

Multidisciplinary Digital Publishing Institute

Resumen

The wear behavior of the Mg-3wt.% Zn-0.4wt.% Ca (ZX30) alloy was tested using a pin-on-disc configuration with AZ31 alloy discs as counterparts under dry sliding conditions. The ZX30 alloy was tested in different states: as-cast, solution-treated, peak-aged, and over-aged. Wear rates and friction coefficients were measured at different loads and sliding speeds. Abrasion and oxidation were the main wear mechanisms found in all the conditions tested. Moreover, aluminum oxides were detected on the worn surfaces, which indicates the presence of an adhesive wear mechanism. The wear behavior of the studied ZX30 alloy showed a greater tendency towards oxidative wear than other Mg alloys, and the microstructure observed strongly affected the wear behavior.

Descripción

Citación

Pulido-González, N.; García-Rodríguez, S.; Torres, B.; Rams, J. Effect of Heat Treatment on the Dry Sliding Wear Behavior of the Mg-3Zn-0.4Ca Alloy for Biodegradable Implants. Materials 2023, 16, 661. https://doi.org/10.3390/ma16020661
license logo
Excepto si se señala otra cosa, la licencia del ítem se describe como Attribution 4.0 Internacional